Bridging agent HX213 as solvent type PA, PU special bridging agent, because of the production in the reaction process lively uniform bonding timely closed, thus forming a denser mesh structure with hydroxyl and carboxyl crosslinked (not rebound, with fastness) film, toughness, adhesion to superior, and mixing on the glue after the colloid stored for a long time, is widely used in coating, composite, flocking, printing and other industries (equipment for rolling, and the amount of not more than 5% of the amount of glue,), can effectively improve the fastness of crosslinking solvent type PA and PU and the bottom cloth, the product is greatly improved wear resistance, tear strength, water resistance the performance index.

Appearance: colorless transparent to yellowish viscous liquid

Viscosity: 200~1000cps viscosity test specification: NDJ-1/2# turn（30℃）

Solid content: ≥65％ Solid part test method: 3g sample/105℃/3hr

Ph value: 8.5~11.5

Solubility: dissolving in general solvents at any proportion

Packing: 20 kg net, drum

Warehousing and transportation: bridging agent HX213 is easy to react to water. Therefore, it is advisable to seal completely in storage and prevent bridge erection from hardening. Because organic solvent is added, it should be stored in a cool and ventilated place and prevent fire sources.

Caution: before using this product, we must strictly test and detect the manufacturing products. Our company is only responsible for the continuity of the product's performance indicators within the allowed fluctuation range.